Ceramic Supper saddle ring (CSSR)
Ceramic Super Intalox saddles (or Ceramic super saddles for short, NOT Koch-Glitsch INTALOX) are the most frequently used high-performance packing which exhibit advantages for most applications in comparison with other packing of different shapes. Ceramic super saddles' smooth surface imparts a high chemical resistance and provides them with a high level of stability. Due to their simple form, Ningbo T.C.I Ceramic Super Intalox saddles can be produced at a relatively low cost. Ningbo T.C.I is the best ceramic super intalox saddles manufacturer, ceramic super inalox saddles supplier for you.
Applications:
T.C.I Ceramic Super Intalox saddles ( similar Koch-Glitsch INTALOX) are widely used as Regenerative Thermal oxidizers, Acid Gas Scrubbers, Dryer Towers, Tail Gas Scrubbers and Impasse Towers.
Specification of ceramic super intalox saddles
| Normal Size |
Approx.Weight |
Surface Area |
Void Fraction(%) |
Dry Packing factor (m-1) |
| lb/ft3 |
Kg/m3 |
ft2/ft3 |
m2/m3 |
| 1" |
25mm |
40 |
645 |
79.5 |
260 |
77 |
570 |
| 1.5" |
38mm |
37.5 |
600 |
64 |
210 |
78 |
430 |
| 2" |
50mm |
35.6 |
570 |
42.8 |
140 |
79 |
277 |
| 3" |
76mm |
36 |
580 |
32 |
105 |
|
|
Ceramic Supper Saddles Chemical Composition
| Composition |
Value |
Composition |
Value |
| SiO2 |
>69% |
CaO |
<0.25% |
| Al2O3 |
15-23% |
MgO |
<0.2% |
| SiO2+Al2O3 |
>92% |
K2O+Na2O |
2-4% |
| Fe2O3 |
<1% |
Other |
<1% |
Physical Properties
| Index |
Unit |
Value |
| Porosity |
Vol % |
1 |
| Specific heat |
KJ/Kg |
840-900 |
| Crush strength |
N/mm2 |
390-420 |
| Specific gravity |
g/cm3 |
2.3-2.45 |
| Acid Resistance |
% |
99.98 |
| Firing temperature |
℃ |
1280 to 1320 |
| Softening point |
℃ |
>1400 |
| Density |
Kg/m3 |
2300-2400 |
| Water absorption |
% |
<0.2 |
| Thermal Expansion |
10-6mm/mm℃ |
4.7 |
| Hardness |
Mohr Scale |
7-8 |
| Comprehensive strength |
Newtons |
5600 |
| Shock strength |
Kgf.cm/cm2 |
1.0-1.5 |
| 